decap:epoxy [2018/02/28 06:55] – [A. Zonenberg etch rate measurement] mcmaster | decap:epoxy [2020/02/27 20:58] – [McMaster live 2019-11-10] mcmaster | ||
---|---|---|---|
Line 132: | Line 132: | ||
One problem from this lack of circulation is that it may create pockets of low concentration acid, leading to corrosion. | One problem from this lack of circulation is that it may create pockets of low concentration acid, leading to corrosion. | ||
+ | |||
+ | ===== McMaster live 2019-11-10 ===== | ||
+ | |||
+ | {{: | ||
+ | |||
+ | Experiments trying to decap COB while keeping PCB intact | ||
+ | |||
+ | TLDR best result | ||
+ | - Cut a polypropylene tube (ie from a microfuge tube) roughly the size you want to expose to acid | ||
+ | - Heat tube up to soften it | ||
+ | - Warm PCB | ||
+ | - Attach hot tube to PCB, letting plastic deform into place | ||
+ | - Let cool a little | ||
+ | - Seal outside of tube with silicone | ||
+ | - Let silicone cure | ||
+ | - Decap with gentle heat on hotplate (maybe 160F max) using 2 WFNA : 1 H2SO4 | ||
+ | |||
+ | Above is a compromise between PP providing the best chemical resistance and silicone providing the best seal | ||
+ | |||
+ | Silicone only experiment | ||
+ | * Made silicon dam by layering up | ||
+ | * Silicone surface cured, but internally didn't always | ||
+ | * Uncured silicone dissolved in WFNA and floated to top. This then cured and blocked the surface | ||
+ | * Interesting, | ||
+ | * Acid may eventually undermine the PCB, but eating the silicone itself came first | ||
+ | * Consider using a lot more silicone than you need to help mitigate acid splashes | ||
+ | * Maybe cover board surface with kapton? | ||
+ | |||
+ | Someone also suggested I should try PTFE gasket. In the past I had tried kapton which didn't work well (acid tended to wick into kapton). Maybe PTFE would repel acid better | ||
Line 222: | Line 251: | ||
* They do the whole chip but avoid die area | * They do the whole chip but avoid die area | ||
* Light Ray - IC Decapsulation | * Light Ray - IC Decapsulation | ||
+ | |||
+ | |||
+ | ===== mcmaster ezlaze ===== | ||
+ | |||
+ | TODO: add pictures, estimate material removal rate | ||
+ | |||
+ | Basically this was too slow to be practical except for very small samples. That said, it did work very well. A quicklase or other higher throughput Nd:YAG system would likely work well | ||
====== Sandblast ====== | ====== Sandblast ====== |