mcmaster:cbm:65ce02-r2 [2021/05/28 02:34] 127.0.0.1 external edit |
mcmaster:cbm:65ce02-r2 [2023/02/16 10:17] (current) |
{{:mcmaster:cbm:65ceo2:die2.jpg?300}} | {{:mcmaster:cbm:65ceo2:die2.jpg?300}} |
| |
[[http://siliconpr0n.org/map/cbm/65ce02/r2_mz_mit20x/|Top metal @ Mit20x]] | [[http://siliconpr0n.org/map/cbm/65ce02-r2/mcmaster_mz_mit20x/|Top metal @ Mit20x]] |
* [[http://siliconpr0n.org/map/cbm/65ce02/single/cbm_65ce02r2_mz_mit20x.jpg|Single]] (12509×10688, 53 MB) | * [[http://siliconpr0n.org/map/cbm/65ce02-r2/single/cbm_65ce02-r2_mcmaster_mz_mit20x.jpg|Single]] (12509×10688, 53 MB) |
| |
| |
{{:mcmaster:cbm:65ceo2:etch1-13_mit20x.jpg?300|}} | {{:mcmaster:cbm:65ceo2:etch1-13_mit20x.jpg?300|}} |
| |
[[http://siliconpr0n.org/map/cbm/65ce02/r2_etch1-13_mit20x/|Etch 1-13 @ Mit20x]] | [[http://siliconpr0n.org/map/cbm/65ce02-r2/mcmaster_etch1-13_mit20x/|Etch 1-13 @ Mit20x]] |
* [[http://siliconpr0n.org/map/cbm/65ce02/single/cbm_65ce02r2_etch1-13_mit20x.jpg|Single]] (12442x10722, 59 MB) | * [[http://siliconpr0n.org/map/cbm/65ce02-r2/single/cbm_65ce02-r2_mcmaster_etch1-13_mit20x.jpg|Single]] (12442x10722, 59 MB) |
| |
{{:mcmaster:cbm:65ceo2:etch1-16_mit20x.jpg?300|}} | {{:mcmaster:cbm:65ceo2:etch1-16_mit20x.jpg?300|}} |
| |
[[http://siliconpr0n.org/map/cbm/65ce02/r2_etch1-16_mit20x/|Etch 1-16 @ Mit20x]] | [[http://siliconpr0n.org/map/cbm/65ce02-r2/mcmaster_etch1-16_mit20x/|Etch 1-16 @ Mit20x]] |
* [[http://siliconpr0n.org/map/cbm/65ce02/single/cbm_65ce02r2_etch1-16_mit20x.jpg|Single]] (12433x10684, 53 MB) | * [[http://siliconpr0n.org/map/cbm/65ce02-r2/single/cbm_65ce02-r2_mcmaster_etch1-16_mit20x.jpg|Single]] (12433x10684, 53 MB) |
| |
{{:mcmaster:cbm:65ceo2:etch1-25_mit20x.jpg?300|}} | {{:mcmaster:cbm:65ceo2:etch1-25_mit20x.jpg?300|}} |
Sometime between etch16 and etch25 I believe a beaker contaminted with nitric was used. This caused unintentional staining of the chip as well as etching in some of the less pure areas of the chip causing pitting. | Sometime between etch16 and etch25 I believe a beaker contaminted with nitric was used. This caused unintentional staining of the chip as well as etching in some of the less pure areas of the chip causing pitting. |
| |
[[http://siliconpr0n.org/map/cbm/65ce02/r2_etch1-25_mit20x/|Etch 1-25 @ Mit20x]] | [[http://siliconpr0n.org/map/cbm/65ce02-r2/mcmaster_etch1-25_mit20x/|Etch 1-25 @ Mit20x]] |
* [[http://siliconpr0n.org/map/cbm/65ce02/single/cbm_65ce02r2_etch1-25_mit20x.jpg|Single]] (12416x10696, 45 MB) | * [[http://siliconpr0n.org/map/cbm/65ce02-r2/single/cbm_65ce02-r2_mcmaster_etch1-25_mit20x.jpg|Single]] (12416x10696, 45 MB) |
| |
| |