- | Copper etch - 70 ml 3% H2O2 + 10 ml conc. HCl. Heat to 70C, agitate with magnetic stirrer. | ||
- | |||
- | Test sample was Altera Stratix IV. Silver or tin plated copper. Plating was gone after <1 min in etchant, metallurgy of the plating was not studied. 20 minutes of etching = 0.13mm removal so 6.5 um/min. This number is likely +/- 30% or so because the temperature of the solution slowly increased over the etch period. | ||